T1  - <i>In-Situ</i> Synthesis of ZSM-5 Catalyst to Form SCR Catalyst Membrane and it&#146;s Application
in NOx Reduction
AU - Binnal, Prakash AU - Manjunath, S.P. AU - Rajashekhara, S. AU - Patil, Jagadish 
JO  - Journal of Engineering and Applied Sciences
VL  - 15
IS  - 19
SP  - 3463
EP  - 3467
PY  - 2020
DA  - 2001/08/19
SN  - 1816-949x
DO  - jeasci.2020.3463.3467
UR  - https://makhillpublications.co/view-article.php?doi=jeasci.2020.3463.3467
KW  - ZSM-5
KW  -SCR catalyst
KW  -COMSOL multiphysics
KW  -X-ray diffraction
AB  - Zeolite Socony Mobil-5 (ZSM-5) is a synthetic
Aluminium silicate zeolite belonging to the pentasil
family of zeolite. The vertices are Al or Si and an O is
assumed to be bonded between the vertices. In the present
work, ZSM-5 was prepared by using Colloidal Silica and
sodium aluminate as silicon and aluminium sources
respectively. Since, ZSM-5 acts as catalyst even at
prolonged high temperature, the ZSM-5 is used for the
Selective Catalytic Reduction of (SCR) of NOx in the
exhaust pipe of diesel engine. A thin film of ZSM-5 was
developed on the metal sheet by hydrothermal method
forms a Selective Catalytic Reduction (SCR) catalyst of
plate type of structure. The characterization of SCR
catalyst is carried by subjecting to X-ray diffraction, BET
test, erosion test. The surface area per unit weight for
uncalcined sample was 40.635 m2/g. The X-ray diffraction
shows that the topology of the prepared silicate-1.