Ahmed Ouari  , Mohamed Guerioune  , Amar Boudour  , Youcef Boumaiza  , 
    Microstructural Evolution in Terms of Porosity in High-Tc Superconductors,
    Asian Journal of Information Technology,
    Volume 5,Issue 12,
    2006,
    Pages 1328-1331,
    ISSN 1682-3915,
    ajit.2006.1328.1331,
    (https://makhillpublications.co/view-article.php?doi=ajit.2006.1328.1331)
    Abstract: The low critical current densities of high-Tc superconductors materials can be related to the microstructural imperfections such as pores and microcracks which reduce the effective current carrying cross section. The present study examines the characterisation of the state of microstructure and its evolution during thermal treatment of YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7- </SUB>. The dilatometric analysis was used to study the shrinkage mechanism during sintering. The microstructure of the sintered samples was characterised in terms of pores distribution and apparent density. Open porosity was measured by mercury porosimeter. In order to compare the results, ultrasonic characterisation such as the longitudinal and transverse wave velocities in the ceramic was carried out.  From an ultrasonic point of view, these microstructural features act as inhomogeneities, then the measured ultrasonic parameters will depend on the geometrical arrangement of the microstructure (pores have an effect both on Young’s modulus and attenuation).
    Keywords: Superconductors;porosity;acoustic signature V(z);velocities;elastic parameters